3004 Aluminum Bar

‹

›

‹

  • 3004 Aluminum Bar
  • 3004 Aluminum Bar
  • 3004 Aluminum Bar
  • 3004 Aluminum Bar

›

3004 Aluminum Bar

Introduction：
1. Low MOQ and Flexible Production Ability.
2. Quick delivery and standard industry exporting package.
3. Best service with quick  reply 
4. OEM and ODM, welcome customers to visit our factory for better understanding;
5. Value friendship and trustworthy, devote to provide long-term service to our distinguished customers.

Inquiry
Contact us

Product Introduction

3004 aluminium alloy is an alloy in the wrought aluminium-manganese alloys family (3000 or 3xxx series). It is similar to the 3003 alloy, except for the addition of approximately 1% magnesium. It can be cold worked (but not, unlike some other types of aluminium alloys, heat treated) to produce tempers with a higher strength but a lower ductility. Like most other aluminium-manganese alloys, 3003 is a general-purpose alloy with moderate strength, good workability, and good corrosion resistance. It is commonly rolled and extruded, but typically not forged. As a wrought alloy, it is not used in casting.
3004 Aluminium Alloy Composition by Mass %
AlMgSiFeCuZnMnRemainder
95.6 to 98.2%0.8 to 1.3%0.3% max0.7% max0.25% max0.25% max1.0 to 1.5%0.15% max


Machinability

Aluminium / Aluminum  3004 alloy has good machinability in the hard temper. Oil lubricant is used for performing machining operations.

Forming

Aluminium / Aluminum  3004 alloy can be formed using conventional hot working or cold working methods.

Welding

The Aluminium / Aluminum  3004 alloy can be welded using TIG or MIG welding techniques.

Heat treatment

Aluminium / Aluminum  3004 alloy is a non-heat treatable alloy.

Forging

Aluminium / Aluminum  3004 alloy is forged at temperatures ranging from 372 to 510°C (700 to 950°F).

Hot Working

Aluminium / Aluminum  3004 alloy is hot worked at 260 to 483°C (500 to 900°F).

Cold Working

Aluminium / Aluminum  3004 alloy can be cold worked up to 75% reduction of area using conventional techniques. This process should be followed by annealing if it is cold worked beyond 75% reduction of area.

Annealing

Aluminium / Aluminum  3004 alloy is annealed at 344°C (650°F) followed by cooling in air.

Hardening

Aluminium / Aluminum  3004 alloy can be annealed by cold working.

Applications

Aluminium / Aluminum  3004 alloy is used in sheet metal work. It is also used in manufacturing storage tanks.


Application

Construction/Indutry/Building/Chemical/Auto

The alloy 3004 is commonly used in the making of beverage cans. It was developed to satisfy the need for thinner gauges in can-stock, and thereby to some extent replaced its predecessor 3003 alloy in the making of beverage cans. Can-stock can be made thinner due to the addition of 1% magnesium, which contributes in solid solution strengthening.